Porous Carbon Foam High Conductivity Carbon Foam for Electrode & Filtration

Porous Carbon Foam High Conductivity Carbon Foam for Electrode & Filtration

1. Low density, high strength
2. It can be made into high or low thermal conductivity materials
3. It has good thermal shock resistance and can resist the shock of temperature sudden change of 1 250 ℃
4. High temperature and corrosion resistance
5. Pore size can be foamed according to customer's requirements
6, the processing performance is good, can use all kinds of common adhesives to bond, so that the carbon foam block is not restricted, and more easily formed a complex structure, on the surface of the carbon foam can be plated metal materials.
7. Flexible material design. The performance design can be changed in a wide range, and the performance of the foam carbon can be achieved by engineering methods to meet the needs of different density, hole and hole connection.

Thickness	0.1-25mm
Pore Size(PPI)	15/20/30/50/90/100
Purity(%)	99.99
Porosity(%)	50-98
Surface desity(g/m2)	280-3000
Size(mm)	10x10, 50x50,100x100, 200x200, Can be customized
Density(g/cm3)	0.2~1.0
Compressive strength(Mpa)	8~12
Tensile modulus(Mpa)	300~500
Thermal expansion coefficient (ppm/℃)	5.0
Thermal conductivity(W/m.k)	25~80
Resistivity(Ω·m)	1.0×10﹣2~10﹣5
Maximum operating temperature	600 ℃ (in air) 3000 ℃ (in inert gas)

Dimensions

0.5mm*100mm*100mm	0.6mm*100mm*100mm	0.7mm*100mm*100mm
0.8mm*100mm*100mm	0.9mm*100mm*100mm	1.0mm*100mm*100mm
1.2mm*100mm*100mm	1.5mm*100mm*100mm	2.0mm*100mm*100mm
2.5mm*100mm*100mm	3.0mm*100mm*100mm	The size can be customized