98% Porosity Porous Materials Carbon Foam/Carbon Metal Foam C Foam For Electrode Sheet

98% Porosity Porous Materials Carbon Foam/Carbon Metal Foam C Foam For Electrode Sheet

1. Low density, high strength
2. It can be made into high or low thermal conductivity materials
3. It has good thermal shock resistance and can resist the shock of temperature sudden change of 1 250 ℃
4. High temperature and corrosion resistance
5. Pore size can be foamed according to customer's requirements
6, the processing performance is good, can use all kinds of common adhesives to bond, so that the carbon foam block is not restricted, and more easily formed a complex structure, on the surface of the carbon foam can be plated metal materials.
7. Flexible material design. The performance design can be changed in a wide range, and the performance of the foam carbon can be achieved by engineering methods to meet the needs of different density, hole and hole connection.

Density: 0.2 ~ 1.0g/cm3 

porosity: 30 ~ 80%

Aperture: 0.01-6mm

Compressive strength: 8-12mpa

Compression modulus: 300-620mpa

Tensile strength: 2-5mpa

Tensile modulus: 300 ~ 500MPa 

thermal expansion coefficient: 5.0ppm / ℃

Thermal conductivity: 25 ~ 80W / m.k

Resistivity: 1.0 × 10-2 ~ 10-5 Ω· M

Maximum operating temperature: 600 ℃ (in air), 3000 ℃ (in inert gas)

0.5mm*200mm*300mm	1mm*200mm*300mm	1.5mm*200mm*300mm
2mm*200mm*300mm	2.5mm*200mm*300mm	3mm*200mm*300mm
4mm*200mm*300mm	5mm*200mm*300mm	6mm*200mm*300mm
7mm*200mm*300mm	8 to 10mm*20mm*300mm	The size can be customized